Investigation of The Effect of Cr2O3 Particles on Al-Si Matrix Composites Produced by Powder Metallurgy

Abstract

In this study, composite material with Al-12Si (wt%) matrix was produced by powder metallurgy (PM) method. Al-12Si powder was mixed by adding 5, 10 and 15wt% Cr2O3 powder. Al-12Si+ Cr2O3 powder mixture were pressed unidirectional with 500MPa pressure in a cylindrical mold and sintered at 500 ºC. After sintering, optical microstructure (OM), Scanning Electron Microscope (SEM), Energy Dispersive Spectrometer (EDS) and microhardness analyzes of the samples were made. When the results were examined, it was observed that a porous structure was formed in all of the samples. Moreover, the lowest hardness was measured in the sample added %15wt Cr2O3 powder sintered at 500 ºC.