    The Mechanical and Thermal Behavior of Electrostatic Powder Coating Waste Reinforced Epoxy Composites

    Thumbnail
    View/Open
    Tam Metin/Full Text (1.533Mb)
    Date
    2022
    Author
    DOĞAN, Akar
    KISMET, Yılmaz
    Metadata
    Show full item record
    Abstract
    The present study investigates the mechanical and thermal behavior of polyurethane electrostatic powder coating waste reinforced epoxy composites. Different percentages of electrostatic powder coating waste (3, 6, and 9 wt. %) reinforced epoxy composites were manufactured. The mixture of polyurethane powder coating waste and epoxy was mixed with a magnetic stirrer to ensure that the polyurethane powder coating waste was dispersed well in the epoxy, and then the mixture was placed under vacuum and air bubbles were removed. Tensile and three-point tests were performed to determine the changes in the mechanical properties of the materials, and thermogravimetric analysis was conducted to determine the thermal properties. In addition, images were taken with scanning electron microscopy for morphological features. The study revealed that the three-point flexural strength was increased by up to 8% and 15%, respectively, in the samples with 3 wt% and 6 wt% powder coating waste additives. The material's tensile strength decreased by up to 27% with powder coating waste reinforcement. However, the opposite trend was observed in the modulus of elasticity. Additionally, no significant difference was observed in the thermal properties of the materials. Also, from scanning electron microscopy analysis, it was observed that the inclusion of powder coating waste changed the damage mechanism of the material.
    URI
    http://dspace.beu.edu.tr:8080/xmlui/handle/123456789/14708
    Collections
    • Cilt 11, Sayı 3 (2022) [22]





    Creative Commons License
    DSpace@BEU by Bitlis Eren University Institutional Repository is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 4.0 Unported License..

    DSpace software copyright © 2002-2016  DuraSpace
    Contact Us | Send Feedback
    Theme by 
    Atmire NV
     

     




    | Yönerge | Rehber | İletişim |

    sherpa/romeo

    Browse

    All of DSpaceCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsBy TypeThis CollectionBy Issue DateAuthorsTitlesSubjectsBy Type

    My Account

    LoginRegister

    DSpace software copyright © 2002-2016  DuraSpace
    Contact Us | Send Feedback
    Theme by 
    Atmire NV